This MedLibrary.org supplementary page on Bayer process is provided directly from the open source Wikipedia as a service to our readers. Please see the note below on authorship of this content, as well as the Wikipedia usage guidelines. To search for other content from our encyclopedia supplement, please use the form below:
Related Sponsors
The Bayer process is the principal industrial means of refining bauxite to produce alumina.
Bauxite, the most important ore of aluminium, contains only 30-54% alumina, Al2O3, the rest being a mixture of silica, various iron oxides, and titanium dioxide[1]. The alumina must be purified before it can be refined to aluminium metal. In the Bayer process, bauxite is digested by washing with a hot solution of sodium hydroxide, NaOH, at 175 °C. This converts the alumina to aluminium hydroxide, Al(OH)3, which dissolves in the hydroxide solution according to the chemical equation:
The other components of bauxite do not dissolve. The solution is clarified by filtering off the solid impurities. The mixture of solid impurities is called red mud, and presents a disposal problem. Next, the hydroxide solution is cooled, and the dissolved aluminium hydroxide precipitates as a white, fluffy solid. When then heated to 1050°C (calcined), the aluminium hydroxide decomposes to alumina, giving off water vapor in the process:
A large amount of the alumina so produced is then subsequently smelted in the Hall-Héroult process in order to produce aluminium.
History
The Bayer process was invented in 1887 by Karl Bayer. Working in Saint Petersburg, Russia to develop a method for supplying alumina to the textile industry (it was used as a mordant in dyeing cotton), Bayer discovered in 1887 that the aluminium hydroxide that precipitated from alkaline solution was crystalline and could be easily filtered and washed, while that precipitated from acid medium by neutralization was gelatinous and difficult to wash.
A few years earlier, Henry Louis Le Chatelier in France developed a method for making alumina by heating bauxite in sodium carbonate, Na2CO3, at 1200°C, leaching the sodium aluminate formed with water, then precipitating aluminium hydroxide by carbon dioxide, CO2, which was then filtered and dried. This process was abandoned in favor of the Bayer process.
The process began to gain importance in metallurgy together with the invention of the electrolytic aluminium process invented in 1886. Together with the cyanidation process invented in 1887, the Bayer process marks the birth of the modern field of hydrometallurgy
Today, the process is virtually unchanged and it produces nearly all the world's alumina supply as an intermediate in aluminium production.
See also
References
- ^ Harris, Chris; McLachlan, R. (Rosalie); Clark, Colin (1998). Micro reform — impacts on firms: aluminium case study. Melbourne: Industry Commission. ISBN 0-646-33550-2.
- Habashi, F. "A short history of hydrometallurgy", Hydrometallurgy 79, pp. 15-22, 2005.
Wikipedia content modification information:
- This page was last modified on 16 July 2008, at 09:27.
Wikipedia Authorship and Review
Wikipedia content provided here is not reviewed directly by MedLibrary.org. Wikipedia content is authored by an open community of volunteers and is not produced by or in any way affiliated with MedLibrary.org.
Wikipedia Usage Guidelines
This article is licensed under the GNU Free Documentation License. It uses material from the Wikipedia article on "Bayer process".
The URL for this specific entry is:
All Wikipedia text is available under the terms of the GNU Free Documentation License. (See Copyrights for details). Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc.